Material applicable ASTM standard . Selection

 

 

ASTM Casting Materials

Material

ASTM
Casting
SPEC

Service

Carbon Steel

ASTM A216
Grade WCB

Non-corrosive applications including water, oil and gases at temperatures between -20°F (-30°C) and +800°F (+425°C)

Low Temp
Carbon Steel

ASTM A352
Grade LCB

Low temperature applications to -50°F (-46°C). Not for use above +650°F (+340°C).

Low Temp
Carbon Steel

ASTM A352
Grade LC1

Low temperature applications to -75°F (-59°C). Not for use above +650°F (+340°C).

Low Temp
Carbon Steel

ASTM A352
Grade LC2

Low temperature applications to -100°F (-73°C). Not for use above +650°F (+340°C).

3.1/2% Nickel
Steel

ASTM A352
Grade LC3

Low temperature applications to -150°F (-101°C). Not for use above +650°F (+340°C).

1.1/4% Chrome
1/2% Moly Steel

ASTM A217
Grade WC6

Non-corrosive applications including water, oil and gases at temperatures between -20°F (-30°C) and +1100°F (+593°C).

2.1/4% Chrome

ASTM A217
Grade C9

Non-corrosive applications including water, oil and gases at temperatures between -20°F (-30°C) and +1100°F (+593°C).

5% Chrome
1/2% Moly

ASTM A217
Grade C5

Mild corrosive or erosive applications as well as non-corrosive applications at temperatures between -20°F (-30°C) and +1200°F (+649°C).

9% Chrome
1% Moly

ASTM A217
Grade C12

Mild corrosive or erosive applications as well as non-corrosive applications at temperatures between -20°F (-30°C) and +1200°F (+649°C).

12% Chrome
Steel

ASTM A487
Grade CA6NM

Corrosive application at temperatures between -20°F (-30°C) and +900°F (+482°C).

12% Chrome

ASTM A217
Grade CA15

Corrosive application at temperatures up to +1300°F (+704°C)

316SS

ASTM A351
Grade CF8M

Corrosive or either extremely low or high temperature non-corrosive services between -450°F (-268°C) and +1200°F (+649°C). Above +800°F (+425°C) specify carbon content of 0.04% or greater.

347SS

ASTM 351
Grade CF8C

Primarily for high temperature, corrosive applications between -450°F (-268°C) and +1200°F (+649°C). Above +1000°F (+540°C) specify carbon content of 0.04% or greater.

304SS

ASTM A351
Grade CF8

Corrosive or extremely high temperatures non-corrosive services between -450°F (-268°C) and +1200°F (+649°C). Above +800°F (+425°C) specify carbon content of 0.04% or greater.

304L SS

ASTM A351
Grade CF3

Corrosive or non-corrosive services to +800F (+425°C).

316L SS

ASTM A351
Grade CF3M

Corrosive or non-corrosive services to +800F (+425°C).

Alloy-20

ASTM A351
Grade CN7M

Good resistance to hot sulfuric acid to +800F (+425°C).

Monel

ASTM 743
Grade M3-35-1

Weldable grade. Good resistance to corrosion by all common organic acids and salt water. Also highly resistant to most alkaline solutions to +750°F (+400°C).

Hastelloy B

ASTM A743
Grade N-12M

Is well suited for handling hydrofluoric acid at all concentrations and temperatures. Good resistance to sulphuric and phosphoric acids to +1200°F (+649°C).

Hastelloy C

ASTM A743
Grade CW-12M

Good resistance to span oxidation conditions. Good properties at high temperatures. Good resistance to sulphuric and phosphoric acids to +1200°F (+649°C).

Inconel

ASTM A743
Grade CY-40

Very good for high temperature service. Good resistance to spanly corrosive media and atmosphere to +800°F (+425°C).

Bronze

ASTM B62

Water, oil or gas: up to 400°F. Excellent for brine and seawater service.

Material

ASTM
Casting
SPEC

Service

 

Table 1. Valve Body Materials
  ASME - -
CATEGORY  
  Specification Grade Material Group Nominal-Des- ignation
Carbon Steel SA-216 WCC 1.2 S M-n Si
SA-352 LCC(2) 1.2 S M-n Si
SA-350 LF2 1.1 C Mn- Si
Alloy Steels SA-217 WC6 1.9 1 1/4Cr 1/2- Mo
WC9 1.1 2 1/-4Cr 1-Mo
C12A 1.15 9Cr 1 -Mo V
Stainless Steel SA-351 CF8M 2.2 16Cr 1- 2 Ni 2- Mo
CF8 2.1 18- Cr 8 N- i
CF8C 2.11 18C-r 10 N-i Cb
CF3M 2.2 16Cr-12 Ni-2Mo
CG8M 2.2 19Cr 10 Ni 3Mo
CK3MCuN 2.8 - -
20Cr 18 Ni 6Mo
SA-995 CD3MN(3) 2.8 22C-r 5 N- i 3Mo-N
(Grade 4A)
CD3MWCuN 2.8 25Cr 7 Ni 3.5Mo-Cb
(Grade 6A)
1. WCC is a standard substitute for WCB material.
2. LCC is a standard substitute for LCB material.
3. Listed as A351-CD3MN in B16.34-2013.

 

 